Tipo do documento: TCC
Título: Ressonância plasmônica de nanopartículas de prata em madeira de Hevea brasiliensis
Autor: Soares, Sabrina Alvarenga
Latorraca, João Vicente de Figueiredo
Latorraca, João Vicente de Figueiredo;Santos, Glaycianne Christine Vieira dos;Pace, José Henrique Camargo;Castro, Jonnys Paz
Palabras clave: Nanotecnologia;Seringueira;Plasmon
Fecha de publicación: 13-nov-2018
Resumen: A madeira de Seringueira é considerada de baixa durabilidade natural por apresentar alta susceptibilidade ao ataque de fungos e insetos, e também alta instabilidade dimensional. Para evitar que problemas como esse ocorram, é recomendável tratar a madeira recém cortada ou submetê-la ao processo de secagem de forma adequada. Os objetivos desse estudo foram verificar o efeito da ressonância plasmônica em madeiras de Hevea brasiliensis impregnadas com nanopartículas de prata e analisar a influência desse tratamento no processo de secagem. A madeira utilizada foi do clone de seringueira tri composto (PB311-MDF180), de modo que a madeira foi submetida ao processo de impregnação de nanopartículas. No processo com prévia aplicação de vácuo (750 mmHg/30 minutos), as amostras ficaram imersas na solução de nanopartículas de prata a uma concentração de 22 ppm (Tratamento III) e 100 ppm (Tratamento IV). As amostras que não passaram pelo vácuo, ficaram imersas por 1h na solução de 100ppm de nanopartículas de prata (Tratamento II e V), e as amostras controle foram apenas imersas em água e sem vácuo (Tratamento I). No processo de secagem foi utilizado um aparelho composto por um sistema que consiste em um irradiador personalizado projetado usando quatro diodos emissores de luz de ~435 nm. A cada 10 minutos, o peso e a temperatura eram medidos e depois de estabilizadas, as amostras foram levadas para estufa para obtenção do peso seco e determinação da umidade final. A excitação com fontes LED revela-se uma maneira simples e econômica de promover reações assistidas por plasmon. O efeito da ressonância plasmônica pôde ser observado nas análises, onde as amostras impregnadas com nanoparticulas de prata apresentaram valores mais altos de temperatura final e mais baixos de umidade final, comprovando que a energia absorvida resultou em uma conversão altamente eficiente de luz em calor na superfície das nanopartículas, influenciando no processo de secagem.
Abstract: The wood of rubber tree is considered of low natural durability because it presents high susceptibility to the attack of fungi and insects, and also high dimensional instability. To avoid problems such as this, it is advisable to treat the freshly cut wood or submit it to the drying process. The objectives of this study was to verify the effect of plasmon resonance in Hevea brasiliensis wood impregnated with silver nanoparticles and to analyze the influence of this treatment on the drying process. The rubber wood used was of the clone tri compound (PB311-MDF180), so that the wood was subjected to the impregnation process of nanoparticles. In the process with previous vacuum application (750 mmHg / 30 minutes), the samples were immersed in the solution of silver nanoparticles at a concentration of 22 ppm (Treatment III) and 100 ppm (Treatment IV). The samples that did not pass through the vacuum were immersed for 1 hour in the solution of 100ppm silver nanoparticles (Treatment II and V), and the control samples were only immersed in water and without vacuum (Treatment I). In the drying process an apparatus consisting of a system consisting of a custom irradiator designed using four ~ 435 nm light emitting diodes was used. Every 10 minutes, the weight and temperature were measured and after stabilization, the samples were taken to the oven to obtain the dry weight and final humidity determination. The excitation with LED sources proves to be a simple and economical way of promoting assisted plasma reactions. The effect of plasmon resonance could be observed in the analyzes, where samples impregnated with silver nanoparticles presented higher values of final temperature and lower values of final humidity, proving that the energy absorbed resulted in a highly efficient conversion of light to heat on the surface of the nanoparticles, influencing the drying process.
URI: https://rima.ufrrj.br/jspui/handle/20.500.14407/5533
Aparece en las colecciones:TCC - Engenharia Florestal

Se for cadastrado no RIMA, poderá receber informações por email.
Se ainda não tem uma conta, cadastre-se aqui!

Ficheros en este ítem:
Fichero Descripción TamañoFormato 
Monografia - Sabrina Alvarenga Soares (final 2).pdf1.01 MBAdobe PDFVista previa
Visualizar/Abrir


Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.